Top Grade Acetic Neutral Silicone Sealant Tool Gum for Plastic

• CAS No.: 9009-54-5
• Formula: C6h18osi2
• EINECS: 9009-54-5
• Bonding Function: Construction, Fiber & Garment, Footwear & Leather
• Morphology: Cream
• Application: Automobile, Construction, Woodworking, Footwear & Leather, Fiber & Garment, Packing
• Model NO.: MPH102
• Material: Silicone
• Classification: Room Curing
• Main Agent Composition: Silicone
• Characteristic: Cream
• Promoter Composition: Filler
• Composition: Organic Material
• Color: White
• Item No.: Mph102(280ml/PC)
• Item Name: Acid Silicone Sealant
• Appearance: Cream
• Density: 1.34-1.42
• Extrusion,Ml/Min: More Than 400
• Surface Dry Time,mm: 5-20
• Shore a(Hsa): 20-40
• Bonding Destroy Area%: Less Than 10
• Elastic Recover Rate: More Than 80
• Extend Bonding Rate: 60% No Damage
• Solidify Speed mm/24h: 3-8
• Transport Package: Standard Export Carton Packing
• Specification: SGS
• Trademark: MAGPOW
• Origin: Hunan, China
• HS Code: 3506100090
• Production Capacity: 5000 Cartons / Week

Product Description

280ml/300ml Top Grade Acid Silicone Sealant Waterproof Multipurpose 

Feature:
This product is neutrality solidifies, has the characteristics of
high viscosity, the medium module, the high flexibility high strength, outstanding aging resistance, performance fine. There are colors of transparent, gray, porcelain white.
Main Composition:
α,ω-Dihydroxyl Methyl Silicone

Scope Of Application:
This product can be widely used, available in bonding of glass, rubber, lumber, ceramics, metal and textile fiber surface; This product not suitable to use in seep out the fat, the plasticizer or the solvent material surface; in the airtight place and the rime not , successive years immerses or all year long the moist place.

Using Method:
1.Clean the surface to get rid of the rust, oil, or any dirty.
2.Cut the cap point, twists the cap mouth, cut at 45 degree angle bevelling according to need.
3.In order to get the smooth glue, hold the bottle at 45 degree angle, squeeze the glue through cap mouth.
4.If further sealing needed, please finished operation within 5 minutes, wipe off the surplus glue with dry tissue.
5.After completely solidify, amend the glue by knife.

Warning:
1,This product will release a few acetic acid in the solidification process, the working conditions should maintain ventilate.
2,Do not put within kid's reach, non-toxic after solidifies completely, avoid eye contact before solidification, if touches the eye carelessly, use massive water to wash, if serious go to see a doctor.
3,When operation, must hold the glue steadily, cannot separate, guards against mixes in the air and form bubble , affects the seal effect.
4,After operation, take off the cap mouth immediately, close the packing cover tightly to prevent the moisture enter and cause solidification. Wipe off the glue left at glue mouth.
5,This product should be operated at temperature 5-40ºC,relative humidity 40-80%





Using Method:
1. Eliminates the rubber spot surface with the cotton yarn the dust, the greasy dirt and water.
2. Dust the metal foil behind the aluminum tube, punctures with the sharp shape the orifice, turns on lathe the plastic rubber mouth, according to needs the size in the rubber mouth place aperture. Put the glue on the joint place and fix the size within 15 minutes.
3. The operation temperature is generally at 5-35ºC,humidity at 65%-75% is the best.

Warning:
1. Use up once opened .Otherwise must seal the preservation strictly.
2. Avoids the skin or the eye contact, if contacts carelessly, uses the massive clear water to flush and to go see a doctor immediately.
3. When is been heavy by the cementation work piece or needs to move, in the solidification time needs the auxiliary means localization.
4. The working conditions maintain enough ventilate.

Storage And Packing:
1.The product is non-flammable. keep dry and shade,air tight during storage.
2. The shelf life is 12 months from the date of production.

Technical Feature:

Appearance	Unit	Data	Item	Unit	Data
Appearnace	/	Black even cream	Shear Strength	MPa	≥ 4.0
Density	g/cm 3	1.2 ± 0.1	Elasticrecovery rate%	%	≥ 100
Surface dry time	Min	20-60	Flexibility	%	≥ 400
Solidify speed	mm/24h	2-8	Displacement ability	± %	12.5
Dropping ability(N Type)	Mm	0	Shao's AHardness	/	40-60
Low Temperature	ºC	-40 ºC	Leakage rate	/	0
Peel Strength	MPa	≥ 6.0	Pollution	/	No pollution