Magpow High Temperature Resistance Black Color RTV Acetic Silicone Gasket Maker for Auto

• Customization: Available
• Bonding Function: Instant Adhesive
• Morphology: Cream
• Model NO.: MPB118
• Application: Construction, Woodworking, Footwear & Leather, Fiber & Garment, Packing
• Material: Fiber & Garment
• Classification: Footwear & Leather
• Main Agent Composition: Volatile Solvent Adhesives(Silicone)
• Characteristic: Auto Spare Parts and Hardware
• Color: Black
• Brand Name: Magpow
• Prolapse Distance Vertical: Less Than 3mm
• Prolapse Distance Aclinic: No Distortion
• Density: 0.93-0.98
• Extrusion: More Than 400ml/Min
• Shore a(Hsa): 20-30
• Surface Dry Time: 5-15 Min
• Using Temperature: -40 to 150 Centigrade
• Stock: Full and Can Accept Customer′s Brand
• Transport Package: 85g/Set, 12sets/Inner, 12inners/CTN
• Specification: SGS
• Trademark: MAGPOW
• Origin: Changsha, Hunan
• HS Code: 3506100090
• Production Capacity: 500 Cartons / Week

Product Description

Widely Used Dtlstar Liquid SiliconeAdhesive Glue

Item: MPB118
Specifiction: 85g/set, 12sets/inner, 12inners/CTN
Meas: 67.3*42.8*28.9cm

Main Component:
α , ω -Dyhydroxyl Methyl Silicone

Color:
Transparent, black, grey, blue, red.

Feature of sealant:
This product is one kind of sulfur silicone sealant with one acid component which could be applied at any climate and could take chemical reaction with the water in air rapidly. Good aging-resistant ability, high flexible, perfect performance of high or low temperature resistant. Several machine waster water resistant, good elastic.

Scope of application:
This product is used for sealing of car, gear case of motor, fore-and-art board, water pump, plane flange, cover board of other machine equipment.

Using Method:
1. Cleaning up the surface with the cotton fabric, guarantees the surface not to have the dust, the greasy dirt, the rusty stain and so on.
2. In order to obtain good outward appearance, paste the temporary protection adhesive tape, near the place to be pasted after clean the surface, pull out after paste glue.
3. Pierce the seal with the cap, cover the mouth, cut bevel the tube mouth.
4. Spread the sealant evenly on the place which need to be sealed or bonded. The operation should be continuously, guarantee the sealant continuously squeeze out at cylinder shape, move the glue mouth evenly and slowly, prevent the form of bubble or hole is move too fast.
5. The sealant form shape at approximately 10 minutes, when assembly maintains the gasket thickness, fold gathers the curing at normal temperature 24 hours.

Warning:
1. This product will release a few acetic acid in the solidification process, the working conditions should maintain ventilate.
2. Do not put within kids reach, non-toxic after solidifies completely, avoid eye contact before solidification, if touches the eye carelessly, use massive water to wash, if serious go to see a doctor.
3. When operation, must hold the glue steadily, cannot separate, guards against mixes in the air and form bubble, affects the seal effect.
4. After operation, take off the cap mouth immediately, close the packing cover tightly to prevent the moisture enter and cause solidification. Wipe off the glue left at glue mouth.
5. This product should be operated at temperature 5-40, relative humidity 40-80%

Storage and packing:
1. This product is non-flammable, seal store in 10-27 centigrade cool dry place.
2. The shelf life for top grade acetic gasket maker s 12 months from date of production.
3. Packing 45g/PC, 85g/PC, 85PC+3G promotion in tube.

We are China Adhesive manufacturer. And The adhesive is a compound that adhesives or bonds two items together. Adhesives may come from either natural or synthetic sources. Some modern adhesives are extremely strong, and are becoming increasingly important in modern construction and industry.

No.	Item	Technical Parameter
Top grade	Common grade
1	Appearance	Exquisite well-proportioned cream,no agglomeration, no gelling, no surface solidify, no bubble, hard dispersing
2	Prolapse Distance	Vertical mm	≤ 3
plane	No distortion
3	Density	0.93-0.98	0.93-0.98
4	Extrusion , ml/min	≥ 400	≥ 400
5	Surface setting Time, mm	5-15	5-15
6	Shao's Hardness	20-30	15-30
7	2 3 C Standard extend	≥ 0.4	≥ 0.4
8	Bonding destroy area under under standard condition %	≤ 5	≤ 10
9	Elastic recover rate%	≥ 80	≥ 80
10	Extend bond rate under standard condition	100% no damage	100%no damage
11	Setting time mm/24h	3-8	/
12	Oil-Leakage rate	≤ 2	/
13	applying temperature	-40~ 15 0 C	-40~ 120 C