PUR Edge-Sealing Hot-Melt Wood Door Adhesive Strong Bonding No Glue Line Waterproof Moisture-Proof High Temperature Resistance

• Customization: Available
• Application: Automobile, Construction, Fiber & Garment, Footwear & Leather, Packing, Woodworking
• Color: Milk White Mucus
• Morphology: Mucus
• Brand Name: Magpow
• Commodity: ≥95.0
• Appearance: Viscous Liquid
• Viscosity(25 Centigrade),MPa.S: 15000-25000
• Shear Strength.MPa: ≥2.5
• Solid Content(%): 20-50+-2
• Stock: Full
• Custom-Tailor: Can Accept Customer′s Brand and Design
• CAS No.: C6h18osi2
• Formula: C6h7no2
• Einecs: C3h8n2o
• Characteristic: Volatile Solvent Adhesives
• Promoter Composition: Filler
• Transport Package: 500g, 1kg
• Specification: SGS
• Trademark: MAGPOW
• Origin: Changsha, Hunan
• HS Code: 3506100090
• Production Capacity: 500 Drums / Week

Product Description

PUR Edge-Sealing Hot-Melt Wood Door Adhesive Strong Bonding No Glue Line Waterproof Moisture-Proof High Temperature Resistance:


 

PRODUCT DESCRIPTION
1. It is a one-component wood and panel adhesive . 2. It is a solvent-free, moisture-curable polyurethane adhesive with excellent water, temperature and excellent aging resistance.
TYPICAL APPLICATIONS
1. It is suitable for all parquet and wood flooring types, and also suitable for MDF, Plasterboard, Particle Board, Plywood, etc .
2. It is Industrial used for bonding in the furniture industry .
3. It can be usedd to fix hard timbers (oak, teak, tropical woods, etc).
FEATURE
1. Water- and solvent-free
2. Easy to use
3. Very fast drying
4. Powerful bond strength
5. Outstanding water resistance
6. Various applications
TECHNICAL FEATURES
				Viscous liquid	Q/JL-00-T 001
Appearance
Density		g/cm3	1.13	1.13±0.10	GB/T 13477.2
Solid Content		%	98.4	≥95.0	GB/T 2793	JIS K6833: 1980
Viscosity	///Brookfield	mPa*s	12750	8k~ 18k, 4# v12	GB/T 2794	ASTM D1084: 1988
Curing T ime	//Beech/	min	12	≤30	Q/JL-00-T 024
Shear Strength	6h//Beech/	MPa	4.2	≥2.5	GB/T 7124	ISO 4587: 2003
Shear Strength	24h//Beech/	MPa	4.5	≥3.0	GB/T 7124	ISO 4587: 2003

Notes:                           
 *a, Conditioning, specimen is conditioned under (23±2) ºC, (50±5)% relative humidity if not specified;
*b, Testing Condition, specimen is tested at (23±2) ºC, (50±5)% relative humidity if not specified;
The above data is intended to provide guidance for use and should not be used to write product specifications
*c, Substrate
*d, Others need to be specified.