Double Component Liquid Epoxy Resin for Stone Surface Line Fissures Repair Crack Filling

• CAS No.: 201-177-9
• Formula: C3h4o2
• EINECS: 9009-54-5
• Bonding Function: Liquid
• Morphology: Liquid
• Application: Automobile, Construction, Woodworking, Footwear & Leather, Fiber & Garment, Packing
• Model NO.: 1150
• Material: Epoxy
• Classification: Construction, Fiber & Garment, Footwear & Leather
• Main Agent Composition: Epoxy
• Characteristic: Construction, Fiber & Garment, Footwear & Leather
• Promoter Composition: Curing Agent
• Composition: Epoxy
• Color: Clear
• Viscosity(MPa.S): a: 600-1000, B: 10-30
• Mix Ratio: a:B=3:1
• Pot Life(25ºC,Min): 60-90
• Initial Curing Time(25ºC,H): 3-4
• Shear Strength(Rt48h,MPa): ≥12
• Stock: Full
• Name of Product: Ab Component Epoxy
• Applying Temperature: -30 to 100
• Transport Package: Standard Export Drum Packing
• Specification: 25kg/set
• Trademark: MAGPOW
• Origin: Hunan, China
• HS Code: 3506100090
• Production Capacity: 50000 Cartons / Week

Product Description

Crack Filling Epoxy

Item No.: 1150

Mix ratio by weight: A:B=3:1

 

Application: Mainly used for all kinds of slabs (marble, limestone, granite, sandstone) surface micro-cracks, sand holes, chicken feet, ants road, uneven repair.

No.	Project		Technical data
1	Appearance	A  component	Colorless transparent liquid
		B  component	Colorless transparent liquid
2	Viscosity(mPa·s)	A  component	600-1000
		B  component	10-30
3	Adjusting ratio(A∶B)		3∶1
4	Applicable period(25ºC,min)		60-90
5	Initial curing time(25ºC,h)		3-4
6	Tensile shear strength(RT48h,MPa)		≥7.0

[Instructions]

[Steps for usage]

1.Slabs should be heated or ventilated to remove moisture;

2. Use a brush to remove dust, scum and other impurities from the surface of the stone;

3. Mix glue in A:B=3:1 (by weight ), and mix completely;

4. Scrape back and forth and apply the glue evenly on the surface of the stone;

5. initial curing in 3-4 hours under 25 °C , and proceed to next procedure after 24 hours 

6. Please clean the tools before the glue is uncured.

 

 